Features
|
Raw Materials (Japanese Alumina) |
> 99.7% Al2O3; < 0.01% Fe2O3 |
|
Density |
≥ 3.9 g/m3 |
|
Crystal |
α-alumina |
|
Temperature Resistance |
1400 - 1600 Celsius |
|
Lids |
Available with/without lids |
|
Manufacturing Method |
Pressing |
|
Thermal Shock Resistance |
Good |
|
Coefficient of Thermal Expansion |
Low |
|
Thermal Conductivity |
Good |
|
Chemical Resistance |
Good |
Standard Product Specifications
SKU
Number
Length *
width(mm)
thickness(mm)
MP050
50*50
1/1.5/2/2.5/3/3.5/5/8
MP080A
80*30
1/1.5/2/2.5/3/3.5/5/8
MP080B
80*80
1/1.5/2/2.5/3/3.5/5/8
MP100
100*100
1/1.5/2/2.5/3/3.5/5/8
MP115
115*100
1/1.5/2/2.5/3/3.5/5/8
MP120
120*100
1/1.5/2/2.5/3/3.5/5/8
MP150
150*150
1/1.5/2/2.5/3/3.5/5/8
* material: alumina / ziconia
* only show some spec.
*support customization
*For other sizes and specifications, please contact sales4@johncera.com.mo for more information
Special Sintering Kiln Furniture
1. High purity raw materials ensure the stability of the sintering fixture
2. Good air permeability and super disposable yield
3. Excellent resistance to heat and cold denaturation
4. Good surface finish and smoothness to ensure the sintering of appearance parts
5. Developed high temperature alumina sintered plate used in the field of 1750℃
6. Adopt Japanese alumina raw materials to ensure stable product quality
7. High temperature resistance, long-term use without deformation
8. Excellent long-term service life at super high temperature